MAGNUM HBA

WHY USE IT?

  1. Vickers hardness and modulus of elasticity combined make it ideal for removable partial dentures with hooks.
  2. Easy to polish
  3. Attractive unit yield strength value that allows good resistance to deformation forces
Category:

Description

Composition in %
Cobalt (Co) 62 % Chrome (Cr) 31 % Molybdenum (Mo) 5 % Others C, Si, Mn, Fe

Physical and mechanical features

Solidus-liquidus temperature 1340-1400°C
Thermal expansion coefficient

(25 ÷ 500 °C) 14 x 10-6 K-1

(25 ÷ 600 °C) 14,4 x 10-6 K-1

Melting point 1450°C
Density 8,3 g/cmc
Vickers hardness 389 HV10
Percentage elongation at fracture 6%
Yield load strength 610 MPa
Modulus of elasticity 199 GPa
Ions release in 7 days 0.49 μg/cm2
Colour White
Cytotoxicity test ISO 10993-5 Passed

CE 0123 ACCORDING TO: ISO 9693-1, ISO 22674

Additional information

Typology

Dental Alloys

Use

Skeletonized

Material

Chrome-Cobalt