MAGNUM SATURNO

SKU: 41370017A Category:

Description

Composition in %
Nickel (Ni) 63 % Chrome (Cr) 26 % Molybdenum (Mo) 9 % Silicon (Si) 1,5%

Physical and mechanical features

Solidus-liquidus temperature 1190 ÷ 1303 °C
Thermal expansion coefficient (25 ÷ 500 °C) 13,8 x 10-6 K-1
Melting point 1360 °C
Density 8,2 g/cmc
Vickers hardness 173 HV10
Percentage elongation at fracture 37 %
Yield load strength (Rp0.2) 300 MPa
Modulus of elasticity 197 GPa
Ions release in 7 days 2.7 μg/cm2
Maximium cooking temperature 950°C
Colour White

CE 0425 ACCORDING TO: ISO 9693-1, ISO 22674

Additional information

Typology

Dental Alloys

Use

Skeletonized

Material

Chrome-Cobalt