MAGNUM SUAVE TYPE 5

WHY USE IT?

  1. Easy casting thanks to the low melting range
  2. Excellent specific weight
  3. Easy workability
  4. Excellent polishing
Category:

Description

Composition in %
Cobalt (Co) 40 % Chrome (Cr) 22 % Palladium (Pd) 25% Molybdenum (Mo) 12% Others Si, Mn

Physical and mechanical features

Solidus-liquidus temperature 1232 ÷ 1290 °C
Thermal expansion coefficient (25 ÷ 500 °C) 14,4 x 10-6 K-1 – (25 ÷ 600 °C) 14,9 x 10-6 K-1
Melting point 1340°C
Density  8,9 g/cmc
Vickers hardness 288 HV10
Percentage elongation at fracture 9 %
Yield load strength (Rp0.2) 575 MPa
Modulus of elasticity 181 GPa
Ions release in 7 days 1,8 μg/cm2
Maximium cooking temperature 980°C
Colour White

CE 0123 ACCORDING TO: ISO 9693-1, ISO 22674

Additional information

Typology

Dental Alloys

Use

Ceramic

Material

Semi-Precious