MAGNUM SOLARE TIPO 4

¿POR QUÉ USARLO?

  1. El único en el mercado con dureza Vickers 255
  2. Máxima precisión
  3. Mínimo consumo de las fresas
  4. Menor esfuerzo del mandril de la máquina
SKU: 41300004A-1 Categoría:

Descripción

Composition in %
Cobalt (Co) 66 % Chrome (Cr) 27 % Molybdenum (Mo) 6% Others Si, Mn

Physical and mechanical features

Solidus-liquidus temperature 1307 ÷ 1417 °C
Thermal expansion coefficient (25 ÷ 500 °C) 14,3 x 10-6 K-1 – (25 ÷ 600 °C) 14,5 x 10-6 K-1
Melting point 1470 °C
Density 8,4 g/cmc
Vickers hardness 255 HV10
Percentage elongation at fracture 11 %
Yield load strength (Rp0.2) 395 MPa
Modulus of elasticity 233 GPa
Maximium cooking temperature 980°C
Colour White

CE 0425 ACCORDING TO: ISO 9693-1, ISO 22674

Dimensions
DISC CUT Ø98.5x15mm | DISC CUT Ø98.5×13.5mm | DISC CUT Ø98.5x16mm | DISC PLAIN Ø98.5x10mm | DISC CUT Ø98.5x12mm | DISC CUT Ø98.5x14mm | DISC CUT Ø98.5x18mm | DISC PLAIN Ø98.5x8mm | DISC CUT Ø98.5x20mm | DISC CUT Ø98.5x22mm | DISC CUT Ø98.5x25mm | DISC CUT Ø98.5x24mm | DISC CUT Ø98.5×24.5mm

Información adicional

Tipología

Aleaciones Dentales

Material

Cromo-Cobalto

Formas

Barras, Discos