説明
Composition in %
Nickel (Ni) 63 % Chrome (Cr) 26 % Molybdenum (Mo) 9 % Silicon (Si) 1,5%
Physical and mechanical features
Solidus-liquidus temperature | 1190 ÷ 1303 °C |
Thermal expansion coefficient | (25 ÷ 500 °C) 13,8 x 10-6 K-1 |
Melting point | 1360 °C |
Density | 8,2 g/cmc |
Vickers hardness | 173 HV10 |
Percentage elongation at fracture | 37 % |
Yield load strength | (Rp0.2) 300 MPa |
Modulus of elasticity | 197 GPa |
Ions release in 7 days | 2.7 μg/cm2 |
Maximium cooking temperature | 950°C |
Colour | White |
CE 0425 ACCORDING TO: ISO 9693-1, ISO 22674