Composition in %
Cobalt (Co) 66 % Chrome (Cr) 27 % Molybdenum (Mo) 6% Others Si, Mn
Physical and mechanical features
Solidus-liquidus temperature | 1307 ÷ 1417 °C |
Thermal expansion coefficient | (25 ÷ 500 °C) 14,3 x 10-6 K-1 – (25 ÷ 600 °C) 14,5 x 10-6 K-1 |
Melting point | 1470 °C |
Density | 8,4 g/cmc |
Vickers hardness | 255 HV10 |
Percentage elongation at fracture | 11 % |
Yield load strength | (Rp0.2) 395 MPa |
Modulus of elasticity | 233 GPa |
Maximium cooking temperature | 980°C |
Colour | White |
CE 0425 ACCORDING TO: ISO 9693-1, ISO 22674